ΜΕΛΕΤΗ ΤΩΝ ΦΑΣΕΩΝ ΕΝΩΣΕΩΝ ΤΗΣ ΟΜΑΔΑΣ ΑΙΒ5ΙΙΙΧ8VI

Abstract

THE COMPOUNDS CUIN5TE8 AND AGIN5SE8 HAVE BEEN STUDIED BY MEANS OF COMBINED ELECTRON MICROSCOPY TECHNIQUES. IT HAS BEEN FOUND THAT THE FIRST COMPOUND HAS A TETRAGONAL STRUCTURE AT ROOM TEMPERATURE WITH C/A=2 AND THE SECOND ONE HAS THREE DIFFERENT TETRAGONAL STRUCTURES WITH C/A=2,4 AND 1 RESPECTIVELY. ALL THE STRUCTURES ARE SUPERSTRUCTURES OF A SPHALERITE-LIKE STRUCTURE. AT HIGHER TEMPERATURES,BOTH COMPOUNDS APPEAR WITH A CUBIC SPHALERITE-LIKE STRUCTURE, BECAUSE OF DISORDERING OF THE CATIONS. THE NUMBER AND THE TYPE OF THE ORIENTATION AND TRANSLATION VARIANTS OF THE STRUCTURES HAVE ALSO BEEN STUDIED. FINALLY, THE TRANSITION STATE, BETWEEN THE LONG AND SHORT RANGE ORDER HAS BEEN STUDIED AND ANALYSED.

ΜΕΛΕΤΟΥΝΤΑΙ ΟΙ ΕΝΩΣΕΙΣ CUIN5TE8 KAI AGIN5SE8, ΜΕ ΣΥΝΔΥΑΣΜΟ ΤΕΧΝΙΚΩΝ ΗΛΕΚΤΡΟΝΙΚΗΣ ΜΙΚΡΟΣΚΟΠΙΑΣ. Η ΠΡΩΤΗ ΕΝΩΣΗ ΕΜΦΑΝΙΖΕΤΑΙ ΣΤΗ ΘΕΡΜΟΚΡΑΣΙΑ ΠΕΡΙΒΑΛΛΟΝΤΟΣ ΜΕ ΤΕΤΡΑΓΩΝΙΚΗ ΔΟΜΗ, ΠΟΥ ΕΧΕΙ ΛΟΓΟ C/A=2, ΕΝΩ Η ΔΕΥΤΕΡΗ ΕΜΦΑΝΙΖΕΤΑΙ ΜΕ ΤΡΕΙΣ ΔΙΑΦΟΡΕΤΙΚΕΣ ΤΕΤΡΑΓΩΝΙΚΕΣ ΔΟΜΕΣ ΜΕ ΛΟΓΟΥΣ C/A=2,4 ΚΑΙ 1. ΟΛΕΣ ΟΙ ΔΟΜΕΣ ΕΙΝΑΙ ΥΠΕΡΔΟΜΕΣ ΤΗΣ ΔΟΜΗΣ ΤΥΠΟΥ ΣΦΑΛΕΡΙΤΗ. ΣΕ ΥΨΗΛΟΤΕΡΕΣ ΘΕΡΜΟΚΡΑΣΙΕΣ ΠΑΡΑΤΗΡΗΘΗΚΕ ΚΑΤΑΣΤΡΟΦΗ ΤΗΣ ΤΑΞΕΩΣ ΤΩΝ ΚΑΤΙΟΝΤΩΝ ΚΑΙ ΕΜΦΑΝΙΣΗ ΤΩΝ ΕΝΩΣΕΩΝ ΜΕ ΚΥΒΙΚΗ ΔΟΜΗ ΤΥΠΟΥ ΣΦΑΛΕΡΙΤΗ.ΜΕΛΕΤΟΥΝΤΑΙ ΕΠΙΣΗΣ Ο ΑΡΙΘΜΟΣ ΚΑΙ Ο ΤΥΠΟΣ ΤΩΝ ΠΑΡΑΛΛΑΓΩΝ ΠΡΟΣΑΝΑΤΟΛΙΣΜΟΥ ΚΑΙ ΜΕΤΑΤΟΠΙΣΕΩΣ ΤΩΝ ΔΟΜΩΝ. ΤΕΛΟΣ ΜΕΛΕΤΑΤΑΙ ΚΑΙ ΑΝΑΛΥΕΤΑΙ Η ΜΕΤΑΒΑΤΙΚΗ ΚΑΤΑΣΤΑΣΗ ΜΕΤΑΞΥ ΤΩΝ ΚΑΤΑΣΤΑΣΕΩΝ ΤΑΞΕΩΣ ΕΥΡΕΙΑΣ ΚΑΙ ΠΕΡΙΟΡΙΣΜΕΝΗΣ ΕΚΤΑΣΕΩΣ.