ΜΕΛΕΤΗ ΤΗΣ ΣΚΕΔΑΣΗΣ ΤΩΝ ΗΛΕΚΤΡΟΝΙΩΝ ΑΓΩΓΙΜΟΤΗΤΑΣ ΤΟΥ ΧΑΛΚΟΥ ΣΕ ΑΤΕΛΕΙΕΣ ΑΛΟΥΜΙΝΙΟΥ ΚΑΙ ΣΙΔΗΡΟΥ

Abstract

THE AIM OF THIS DESSERTATION WAS TO STUDY THE EFFECT OF THE PRESENCE OF NON-MAGNETIC IMPURITIES ON THE DEVELOPMENT OF THE KOUDO EFFECT EXIBITED BY MAGNETICIMPURITIES IN A DIPUTE METALIC ALLOY.THE PRESENCE OF A SURFACE IS CONSIDERED A NON-MAGNETIC IMPURITY .A SERIES OF DIPUTE COPPER ALLOWS WERE PREPARED WITH IRON IMPURITIES(MAGNETIC IMPYRITIES)AND THEN A)NON-MAGNETIC ALUMINIUM IMPURITIES WERE ADDED AND B)THE ALLOYS WERE PREPARED IN FORM OF THIN FILMS.THE RESISTIVITY,MAGNETORESISTIVITY AND HALL COEFFICIENT OF THE ALLOYS WERE MEASURED ASA FUCTION OF MAGNETIC FIELD AND TEMPERATURE.IT WAS CONCLUDED THAT THE PRESENCE OF NON-MAGNETIC IMPURITIES DOES NOT AFFECT THE KOUDO EFFECT WHILE WITH THE PRESENCE OFTHE SURFACE IN A THIN FILM THE KOUDO EFFECT DIMINISHES THE THICKNESS OF THE FILM

ΣΚΟΠΟΣ ΤΗΣ ΔΙΑΤΡΙΒΗΣ ΗΤΑΝ ΝΑ ΜΕΛΕΤΗΘΕΙ Η ΕΠΙΔΡΑΣΗ ΠΟΥ ΕΧΕΙ Η ΠΑΡΟΥΣΙΑ ΜΗ ΜΑΓΝΗΤΙΚΩΝ ΠΡΟΣΜΙΞΕΩΝ ΣΤΟ ΦΑΙΝΟΜΕΝΟ KOUDO ΠΟΥ ΕΠΙΔΥΚΝΕΙΟΥΝ ΜΑΓΝΗΤΙΚΕΣ ΠΡΟΣΜΙΞΕΙΣ ΣΕ ΑΡΑΙΑ ΜΕΤΑΛΛΙΚΑ ΚΡΑΜΑΤΑ.ΩΣ ΜΗ ΜΑΓΝΗΤΙΚΗ ΠΡΟΣΜΙΞΗ ΘΕΩΡΕΙΤΑΙ ΚΑΙ Η ΠΑΡΟΥΣΙΑ ΜΙΑΣ ΕΠΙΦΑΝΕΙΑΣ.ΠΡΟΣ ΤΟΥΤΟ ΠΑΡΑΣΚΕΥΑΣΤΗΚΑΝ ΚΡΑΜΑΤΑ ΧΑΛΚΟΥ ΜΕ ΠΡΟΣΜΙΞΕΙΣ ΣΙΔΗΡΟΥ(ΜΑΓΝΗΤΙΚΕΣ ΠΡΟΣΜΙΞΕΙΣ)ΚΑΙ ΣΤΗ ΣΥΝΕΧΕΙΑ Α)ΠΡΟΣΤΕΘΗΚΑΝ ΜΗ ΜΑΓΝΗΤΙΚΕΣ ΠΡΟΣΜΙΞΕΙΣ ΑΛΟΥΜΙΝΙΟΥ ΚΑΙ Β) ΤΑ ΚΡΑΜΑΤΑ ΕΓΙΝΑΝ ΣΕ ΜΟΡΦΗ ΛΕΠΤΩΝ ΥΜΕΝΙΩΝ.ΜΕΛΕΤΗΘΗΚΑΝ Η ΑΝΤΙΣΤΑΣΗ,ΜΑΓΝΗΤΟΑΝΤΙΣΤΑΣΗ,Ο ΣΥΝΤΕΛΕΣΤΗΣ HALL ΣΥΝΑΡΤΗΣΕΙ ΜΑΓΝΗΤΙΚΟΥ ΠΕΔΙΟΥΚΑΙ ΤΗΣ ΘΕΡΜΟΚΡΑΣΙΑΣ ΣΕ ΧΑΜΗΛΕΣ ΘΕΡΜΟΚΡΑΣΙΕΣ.ΔΙΑΠΙΣΤΩΘΗΚΕ ΟΤΙ Η ΠΑΡΟΥΣΙΑ ΜΗ ΜΑΓΝΗΤΙΚΩΝ ΠΡΟΣΜΙΞΕΩΝ ΔΕΝ ΕΠΗΡΕΑΖΕΙ ΤΟ ΦΑΙΝΟΜΕΝΟ KOUDO ΕΝΩ ΑΝΤΙΘΕΤΩΣ ΣΤΑ ΛΕΠΤΑ ΥΜΕΝΙΑ,ΠΑΡΟΥΣΙΑ ΤΩΝ ΕΠΙΦΑΝΕΙΩΝ ΤΟ ΦΑΙΝΟΜΕΝΟ KOUDO ΜΕΙΩΝΕΤΑΙ ΜΕ ΤΟ ΠΑΧΟΣ.